Sellmeier — where it appears

The empirical fit giving a transparent material's refractive index against wavelength as a sum of resonant terms. Differentiating it twice gives the group-delay dispersion, whose zero for fused silica falls at 1,273 nm — a property of where the ultraviolet and infrared absorptions balance rather than anything a designer chose.

Named by 2 essays across one field — each of them below, with the objects they name alongside it.

Cancelling a derivative, and what is left over. How far the focus of a 500 mm lens moves with wavelength, for a single crown element and for a cemented pair of crown and flint whose powers satisfy the achromatic condition. The singlet's focus runs over 18.1 mm across the visible — a fifth of a per cent of its focal length, and utterly ruinous at any useful aperture. The doublet's runs over 2.268 mm, some 8× less, and — this is the whole content of the figure — it is not flat. The condition sets the rate of change of power with wavelength to zero, so the curve is stationary rather than constant: it returns to the corrected focus at exactly 2 wavelengths — 486 nm and 656 nm, which are the two Fraunhofer lines the condition was written at — and departs from it everywhere else, most at 400 nm. That residual is the secondary spectrum, it has the same sign at both ends of the visible, and no pair of ordinary glasses removes it, because two conditions cannot be met with one free ratio.

Two glasses that cancel a derivative

A single lens focuses blue light closer than red, and the difference ruins the image. Cementing a second lens of another glass behind it fixes the fault at two wavelengths and at no others, because the condition sets a slope to zero rather than a value.

optics · Dispersion The wavelength at which a fibre stops smearing a pulse. Group-delay dispersion against wavelength for fused silica, computed by differencing Malitson's Sellmeier fit twice rather than read off a table, in picoseconds of spread per nanometre of source width per kilometre of fibre. The material curve crosses zero at 1273 nm — a property of the glass, fixed by where the ultraviolet and infrared absorptions balance, and not adjustable. Below it a fibre is normally dispersive and above it anomalously so, and at 1550 nm, where silica is most transparent, it is 21.9. The second curve adds a waveguide term, which is negative because a mode confined by a core spreads into the cladding differently at different wavelengths, and which depends on the fibre's geometry rather than on the glass; it is drawn here as a constant offset chosen to put the total zero at 1310 nm, which is what standard single-mode fibre is built to do. The consequence in a system is the thing worth carrying away: a source one nanometre wide sent 100 km through fibre at 1550 nm arrives 1833 picoseconds broader than it left, against 0.0 at the zero. That is the whole reason a network runs at one wavelength rather than another, and the reason the two quantities an engineer wants — lowest loss and zero dispersion — sit at different wavelengths and have to be reconciled by design rather than chosen.

The wavelength a fibre does not smear

Fused silica's index has a second derivative that passes through zero at 1,273 nanometres, and that is not a design choice — it is where the ultraviolet and infrared absorptions balance. A pulse sent at that wavelength arrives the shape it left. A pulse at the wavelength of least loss arrives 1,800 picoseconds wider after a hundred kilometres.

optics · Dispersion

Named alongside it

The objects these essays reach for when they reach for this one.

DispersionAbbe numberChromatic aberrationDepth of focusDiffraction limitFocal lengthGroup velocityGroup velocity dispersionOptical designOptical fibrePulse broadeningRefractive index

All concepts